| Customization: | Available |
|---|---|
| CAS No.: | 24936-68-3 |
| Formula: | [-C6h4c(CH3)2c6h4oco2-]N |
|
Still deciding? Get samples of US$ 0/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Description | Applications | ||||||||
| · Good dimensional stability | · Injection molding | ||||||||
| · Excellent heat stability | · Good mechanical properties balance | ||||||||
| Properties | Test Method | Test Condition | Unit | Typical Values | |||||
| Physical properties | |||||||||
| Specific Gravity | ISO 1183 | 23ºC | g/cm3 | 1.2 | |||||
| MI | ISO 1183 | g/10min | 15 | ||||||
| Ash | ISO 3451 | 800ºC,30min | % | 0 | |||||
| Mechanical properties | |||||||||
| Tensile Strength | ISO 527 | 50mm/min | MPa | 68 | |||||
| (yield) elongation | ISO 527 | 50mm/min | % | 125 | |||||
| Flexural Modulus | ISO 178 | 2mm/min | MPa | 2200 | |||||
| Cantilever beam notched impact strength | ISO180 | 23ºC | KJ/m2 | 60 | |||||
| Non-notched impact strength of cantilever beam | ISO179 | 23ºC | KJ/m2 | 66 | |||||
| Thermal properties | |||||||||
| Heat deflection temperature | ISO 75 | 1.80MPa | °C | 125 | |||||
| Melting Point | DSC | - | C | ||||||
| Other properties | |||||||||
| Flammability | UL94 | 3.2 | V2 | ||||||
| Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type, gate location, gate number, injection molding process, and part thickness. The data will vary with different colors as well. | |||||||||
| Processing Conditions | Range | ||||||||
| Melt Temperature | 304-327ºC | ||||||||
| Mold Temperature | 82.2-121ºC | ||||||||
| Pre-Dry needed | 121ºC, 4-8h | ||||||||
| Note: The above process condition is only for reference. The actual process should be adjusted according to different types of machines, mold design, and product design. | |||||||||